Solar energy is a green, sustainable and clean energy, and solar photovoltaic power generation has become an emerging industry. The solar panel frame is located at the edge of the panel, which supports the panel and protects the panel from external impacts. Since the material is exposed to direct sunlight for long periods of time, such as building exterior walls and roofs, durability against heat and corrosion is required. The frame accounts for about 10% of the solar panel and is mainly made of aluminum alloy.
Compared with the existing aluminum frame, the high-performance engineering plastic material developed by Chuangyongjia has the same durability, but the weight is halved, and the price is very competitive. In addition, this material also has excellent dimensional stability, it can still maintain its shape under temperature changes, and it is not easy to be deteriorated or deformed by the external environment.

#

PA6 20T Color BK

Item GB Units Typical Values
Specific Gravity GB/T 533 g/cm3 1.17
Melt flow index GB/T 3682 g/10min 40
Tensile Strength GB/T 1040 MPa 65
Elongation at break GB/T 1040 % 15
Flexural Strength GB/T 9341 MPa 105
Flexural Modulus GB/T 9341 MPa 3000
Impact Strength, IZOD notched GB/T 1843 23℃，KJ/m2 5.5
Flame Retardancy UL94 1.8mm / V0

PPO FR40Z Color BK

Item GB Units Typical Values
Specific Gravity GB/T 533 g/cm3 1.08
Melt flow index GB/T 3682 g/10min 5
Tensile Strength GB/T 1040 MPa 72
Elongation at break GB/T 1040 % 21
Flexural Strength GB/T 9341 MPa 123
Flexural Modulus GB/T 9341 MPa 2850
Impact Strength, IZOD notched GB/T 1843 23℃，KJ/m2 19
Heat Distortion Temp GB/T 1634 ℃ 145
Flame Retardancy UL94 1.1mm / V0

PPO FRPX130 Color BK

Item GB Units Typical Values
Specific Gravity GB/T 533 g/cm3 1.07
Melt flow index GB/T 3682 g/10min 9
Tensile Strength GB/T 1040 MPa 55
Elongation at break GB/T 1040 % 20
Flexural Strength GB/T 9341 MPa 103
Flexural Modulus GB/T 9341 MPa 2400
Impact Strength, IZOD notched GB/T 1843 23℃，KJ/m2 23
Heat Distortion Temp GB/T 1634 ℃ 130
Flame Retardancy UL94 1.8mm / V0

  Connector Solutions

Engineering plastics have gradually become the main raw material for many connector suppliers due to their key properties such as good toughness, dimensional stability, high impedance, chemical resistance, short-term thermal stability and long-term aging resistance. In recent years, technological trends in connector production and development have dramatically changed the market. With the popularity of high-tight packaging and micronization trends, today's connector designs require higher performance in a smaller space, thus exhibiting thinner wall thicknesses. The plastic material should be able to meet the design of filling the thin wall on the longer connector body, and can maintain the original performance, and also meet the requirements of cost and production time.

#

PA66 RG286NC001N

Item GB Units Typical Values
Specific Gravity GB/T 533 g/cm3 1.59
Melt flow index GB/T 3682 g/10min 20
Tensile Strength GB/T 1040 MPa 145
Elongation at break GB/T 1040 % 6
Flexural Strength GB/T 9341 MPa 210
Flexural Modulus GB/T 9341 MPa 8400
Impact Strength, IZOD notched GB/T 1843 23℃，KJ/m2 13
Flame Retardancy UL94 1.8mm / V0
Glass Fiber Content High Temp Muffle Furnace % 32

PA6 201T Color BK

Item GB Units Typical Values
Specific Gravity GB/T 533 g/cm3 1.26
Melt flow index GB/T 3682 g/10min 90
Tensile Strength GB/T 1040 MPa 50
Elongation at break GB/T 1040 % 14
Flexural Strength GB/T 9341 MPa 90
Flexural Modulus GB/T 9341 MPa 2900
Impact Strength, IZOD notched GB/T 1843 23℃，KJ/m2 5
Flame Retardancy UL94 1.8mm / V0

  Plastic Sheet Solutions

Plastic sheets are sheets made of plastic as raw materials. They are widely used in construction and chemical industries. They are wear-resistant, vibration-resistant, corrosion-resistant, recyclable, strong and resistant to chemical, environmental protection, and building boards. Aging, waterproof, moisture-proof, not easy to deform, reuse and so on. Moreover, the replaced hard plastic pallets can also be recycled and processed, which greatly reduces the cost.

#

FRPC-ABS C3800BK

Item GB Units Typical Values
Specific Gravity GB/T 533 g/cm3 1.18
Melt flow index GB/T 3682 g/10min 30
Tensile Strength GB/T 1040 MPa 60
Elongation at break GB/T 1040 % 22
Flexural Strength GB/T 9341 MPa 110
Flexural Modulus GB/T 9341 MPa 2900
Impact Strength, IZOD notched GB/T 1843 23℃，KJ/m2 54
Flame Retardancy UL94 1.8mm / V0

PA101-G20 板材BK

Item GB Units Typical Values
Specific Gravity GB/T 533 g/cm3 1.26
Melt flow index GB/T 3682 g/10min 25
Tensile Strength GB/T 1040 MPa 115
Elongation at break GB/T 1040 % 6
Flexural Strength GB/T 9341 MPa 180
Flexural Modulus GB/T 9341 MPa 5300
Impact Strength, IZOD notched GB/T 1843 23℃，KJ/m2 9
Glass Fiber Content High Temp Muffle Furnace % 20

PA101-G25 板材BK

Item GB Units Typical Values
Specific Gravity GB/T 533 g/cm3 1.3
Melt flow index GB/T 3682 g/10min 20
Tensile Strength GB/T 1040 MPa 130
Elongation at break GB/T 1040 % 6
Flexural Strength GB/T 9341 MPa 210
Flexural Modulus GB/T 9341 MPa 6400
Impact Strength, IZOD notched GB/T 1843 23℃，KJ/m2 11
Glass Fiber Content High Temp Muffle Furnace % 25

PCFR390BK

Item GB Units Typical Values
Specific Gravity GB/T 533 g/cm3 1.19
Melt flow index GB/T 3682 g/10min 30
Tensile Strength GB/T 1040 MPa 63
Elongation at break GB/T 1040 % 29
Flexural Strength GB/T 9341 MPa 110
Flexural Modulus GB/T 9341 MPa 3000
Impact Strength, IZOD notched GB/T 1843 23℃，KJ/m2 53
Flame Retardancy UL94 1.8mm / V0

   New Energy Solutions

With the rapid development of the automobile industry, especially the rapid development of new energy vehicles (including hybrid, pure electric and hydrogen energy) in recent years, the automobile industry has demanded for lightweight, integration, miniaturization and electrification of auto parts. Also increasing day by day. As an indispensable material in the automotive field, plastics are increasingly becoming the focus of attention for their technology and performance requirements. At the same time, higher requirements are also placed on the material research and development capabilities and rapid response capabilities of material suppliers. Some high-performance new modified plastic materials, such as PPS, PPO, PEEK, etc., as well as other elastomer materials, are promising.

#

PA6101-G15 NC

Item GB Units Typical Values
Specific Gravity GB/T 533 g/cm3 1.2
Melt flow index GB/T 3682 g/10min 10
Tensile Strength GB/T 1040 MPa 110
Elongation at break GB/T 1040 % 9
Flexural Strength GB/T 9341 MPa 165
Flexural Modulus GB/T 9341 MPa 4800
Impact Strength, IZOD notched GB/T 1843 23℃，KJ/m2 30
Glass Fiber Content High Temp Muffle Furnace % 15

PC6330 Color BK

Item GB Units Typical Values
Specific Gravity GB/T 533 g/cm3 1.19
Melt flow index GB/T 3682 g/10min 8
Tensile Strength GB/T 1040 MPa 62
Elongation at break GB/T 1040 % 90
Flexural Strength GB/T 9341 MPa 100
Flexural Modulus GB/T 9341 MPa 2400
Impact Strength, IZOD notched GB/T 1843 23℃，KJ/m2 85
Heat Distortion Temp GB/T 1634 ℃ 133
Flame Retardancy UL94 1.8mm / V0

PC301-G20 blue

Item GB Units Typical Values
Specific Gravity GB/T 533 g/cm3 1.34
Melt flow index GB/T 3682 g/10min 20
Tensile Strength GB/T 1040 MPa 65
Elongation at break GB/T 1040 % 5
Flexural Strength GB/T 9341 MPa 125
Flexural Modulus GB/T 9341 MPa 4200
Impact Strength, IZOD notched GB/T 1843 23℃，KJ/m2 7
Glass Fiber Content High Temp Muffle Furnace % 20
Flame Retardancy UL94 2.0mm / V0

PPO301-G20 BK

Item GB Units Typical Values
Specific Gravity GB/T 533 g/cm3 1.2
Melt flow index GB/T 3682 g/10min 15
Tensile Strength GB/T 1040 MPa 68
Elongation at break GB/T 1040 % 6
Flexural Strength GB/T 9341 MPa 125
Flexural Modulus GB/T 9341 MPa 4200
Impact Strength, IZOD notched GB/T 1843 23℃，KJ/m2 8
Glass Fiber Content High Temp Muffle Furnace % 20
Flame Retardancy UL94 2.0mm / V0